CAN THE SELF-ADHESIVE FLOWABLE COMPOSITE BE SECURELY BONDED TO PRIMARY TOOTH ENAMEL?
[ X ]
Tarih
2021
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Serban Solacolu Foundation
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
This study evaluated the shear bond strength of self-adhesive flowable composite when used with acid etching or a self etch adhesive system. Buccal enamel surfaces on 80 extracted human primary incisors were used and randomly assigned into four groups (n=20); group 1: Vertise (TM) Flow; group 2: Vertise Flow with acid etching; group 3: Vertise Flow with a self-etching bonding agent; group 4: Premise FlowableTM with a total-etch bonding agent as the control group. After 5000 rounds of thermocycling, the bond strength test was performed using a universal testing machine at a crosshead speed of 0.5 mm/min. The fracture analyzes of samples were evaluated using a light stereomicroscope. The results obtained were analyzed via analysis of variance (ANOVA) and Tukey's tests. Statistically significant differences were observed among all groups (P<0.001). Group 1 generated a lower mean shear bond strength (2.63 +/- 1.08 MPa) than those of the other groups [group 2 (7.52 +/- 2.14 MPa), group 3 (5.12 +/- 2.93 MPa), and group 4 (14.18 +/- 2.93 MPa)]. Adhesive failure was the most common failure mode in Vertise Flow groups. Vertise Flow used with a self-etching agent or acid etching exhibited in lower shear bond strength than the control group.
Açıklama
Anahtar Kelimeler
Dental materials, Primary teeth, Self-adhesive flowable composite, Shear bond strength, Vertise (TM) flow
Kaynak
Revista Romana De Materiale-Romanian Journal of Materials
WoS Q Değeri
Q4
Scopus Q Değeri
Cilt
51
Sayı
3