Investigation of Mechanical Properties of Ti6Al4V Alloy Foams produced by Powder Metallurgy Method

Basit Öğe Kaydı
dc.contributor.authorTopcu, İsmail
dc.date.accessioned2026-01-24T12:01:04Z
dc.date.available2026-01-24T12:01:04Z
dc.date.issued2024
dc.departmentAlanya Alaaddin Keykubat Üniversitesi
dc.description.abstractIn this study, it was aimed to production titanium alloy implants, which are widely used in the biomedical industry, as foamed materials under different mechanical alloying and sintering conditions using the powder metallurgy method Tİ6Al4V alloy is good mechanical properties, good biocompatibility properties and good corrosion resistance used as hard tissue replacements and implants. Similar mechanic properties with bone are expected from the implant to work coherently for long cycles of use and without any failure. Especially, elastic modulus of implant must be similar with bones, if not, some damages at bone surface and fallowing repeats of implant surgeries are reported. This situation has a destructive effect on health, finance, and comfort of the patient/user of the implant. In this study, powder metallurgy and space holder removal methods were used to produce porous Ti6Al4V specimens. Throughout the project study different space holder materials and binder agents were used. As weight percent, 20%, 30%, 40%, 60%, 70%, 80% porous specimens were pressed at uniaxial press machine, and sintered to the 850 ºC at argon atmosphere in furnace to reduce the oxidation to the level as low as possible. The E-Modulus values of the specimens reached the desired values with increasing porosity. It was obtained as 88 MPa in the specimen with 80% porosity, decreasing inversely proportionally, especially from the 60% porosity rate.
dc.identifier.doi10.29130/dubited.1062744
dc.identifier.endpage152
dc.identifier.issn2148-2446
dc.identifier.issue1
dc.identifier.startpage143
dc.identifier.trdizinid1303479
dc.identifier.urihttps://search.trdizin.gov.tr/tr/yayin/detay/1303479
dc.identifier.urihttps://doi.org/10.29130/dubited.1062744
dc.identifier.urihttps://hdl.handle.net/20.500.12868/3961
dc.identifier.volume12
dc.indekslendigikaynakTR-Dizin
dc.language.isoen
dc.relation.ispartofDüzce Üniversitesi Bilim ve Teknoloji Dergisi
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_TR-Dizin_20260121
dc.subjectTi6Al4V
dc.subjectPowder metallurgy
dc.subjectSintering
dc.subjectImplant
dc.subjectFoam
dc.titleInvestigation of Mechanical Properties of Ti6Al4V Alloy Foams produced by Powder Metallurgy Method
dc.typeArticle

Dosyalar

Koleksiyon

TR-Dizin İndeksli Yayınlar Koleksiyonu