Impacts of impregnation with fire retardant chemicals on the MOE in bending of some woods

Basit Öğe Kaydı
dc.contributor.authorKeskin, Hakan
dc.contributor.authorMutlu, Erhan
dc.date.accessioned2021-02-19T21:16:28Z
dc.date.available2021-02-19T21:16:28Z
dc.date.issued2017
dc.departmentALKÜ
dc.description.abstractThis study has been performed to determine the effects of impregnation with fire retardant chemical materials on the modulus of elasticity (MOE) in bending of Oriental beech, European oak and Scotch pine wood materials. To achieve this goal, test samples prepared from woods of Oriental beech, European oak and Scotch pine according to TS EN 345 regulations were impregnated with ammonium-sulfate [(NH4)(2)S0(4)], sodium acetate (NaC(2)H3O(2)3H(2)O), aluminum chloride (Al2C6I2H2O), borax [Na(2)B(4)O(7)5H(2)O], boric acid [H-3 BO3] and, borax + boric acid (w:w=%50:50). The modulus of elasticity in bending of impregnated wood samples were determined according to TS EN 408. Consequently, according to wood species; modulus of elasticity in bending was found the highest value at beech (10350 N/mm(2)) and the lowest value at pine wood (9501 N/mm(2)). According to variety of impregnation; modulus of elasticity in bending values were found no statistical difference between control samples and impregnated test samples. Considering the interaction of wood type and process; modulus of elasticity in bending was found the highest value at beech + borax (11450 N/mm(2)) and the lowest value at pine + control samples (8223 N/mm(2)). As a result, in the massive construction and furniture elements that the modulus of elasticity in bending after the impregnation with borax is of great concern, Oriental beech wood materials could be recommended.
dc.identifier.doi10.2339/politeknik.339384
dc.identifier.endpage612en_US
dc.identifier.issn1302-0900
dc.identifier.issn2147-9429
dc.identifier.issue3en_US
dc.identifier.startpage607en_US
dc.identifier.urihttps://doi.org/10.2339/politeknik.339384
dc.identifier.urihttps://hdl.handle.net/20.500.12868/442
dc.identifier.volume20en_US
dc.identifier.wosWOS:000447837400014
dc.identifier.wosqualityN/A
dc.indekslendigikaynakWeb of Science
dc.institutionauthor0-belirlenecek
dc.language.isoen
dc.publisherGazi Univ
dc.relation.ispartofJournal of Polytechnic-Politeknik Dergisi
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.subjectFire retardant chemicals
dc.subjectmodulus of elasticity in bending
dc.subjectimpregnation
dc.subjectwood
dc.titleImpacts of impregnation with fire retardant chemicals on the MOE in bending of some woods